Modeling and Study of Fracture and Delamination in a Packaging Laminate

7th November 2016
No Comment

ABSTRACT In this work, a packaging laminate consisting of LDPE (Low Density Polyethylene), Al-foil (Aluminum foil) is focused, and failure due to necking in substrates and interfacial delamination under loading are considered. A coupled elasto-plasticity damage and fracture constitutive model is combined. The proposed constitutive model is incorporated into the FEM code ABAQUS and utilized […]

Sharing

Study of Shear Dominant Delamination in Thin Brittle-High Ductile Interface

6th September 2016
No Comment

ABSTRACT Thin laminates of Aluminum (Al) foil and Low Density Polyethylene (LDPE) film are essential constituents of food packages where these two substrates are bonded together with a thin layer of LDPE acting as adhesive. Noticeably, Al is a low ductile/quasi brittle material, whereas LDPE is highly ductile. The mechanism of delamination and strength of […]

Sharing

Powerful Modelling Techniques in ABAQUS to Simulate Failure of Laminated composites

30th May 2016
No Comment

ABSTRACT In this study, laminated composites consisting of LDPE (Low Density Polyethylene), Al-foil (Aluminum foil)and an adhesive interface layer is focused. The defects like necking in LDPE, Al-foil layer and interfacial delamination can significantly impact the loading capacity of the laminated material. However, the influence mechanisms of the defects are still unclear, and no appropriate […]